Cerakote Gold 16 oz

Preparation of substrate is crucial for maximum adhesion and performance of this material

1. Remove all coatings, oils, and contaminates from substrate with either a de-greasing chemical and/or by heating substrate to temperatures high enough to remove coatings or contaminates.
2. A blasted profile must be applied to the substrate to remove any rust, scale, or other coatings. This is required to ensure maximum adhesion. For best results use a dry grit material such as aluminum oxide or garnet equivalent to a 100 - 120 mesh size. Mask and plug all areas where coating is not desired. Remove any sharp edges or burrs that may create thin areas or protrude through coating.
3. Place parts in an oven at 450°F for approximately 30 minutes to evaporate any last minute moisture, oils, or contaminates that blasting or contact with skin have deposited on surface. Do not apply any solvents to substrate after a blast profile has been applied.
4. Hang parts to allow for best view and application access. Do not touch parts with bare skin.
5. Make sure the “C” Series products are completely mixed and no solids remain in the bottom of the container. Failure to completely disperse the product will result in poor chemical ratios and product failure.
6. Recommended spray equipment is a HVLP (gravity fed) spray gun. The use of a small spray tip pattern will aid in coating hard to reach areas without excessive build up in surrounding areas. Material does not need to be thinned. Use as received.
7. Blow off substrate with a high-pressure air nozzle to remove any blasting dust left on the surface. Wear safety goggles or face shield for your protection.
8. One applications of product is recommended for a 0.6 to 0.8 mil film thickness. Work from the most difficult surface out to the easiest. This will aid in reducing runs or excessive build up. NOTE: Always spray coating in a well ventilated area. Be aware of over-spray so it will not land on any item that is not to be coated.
9. Parts will be tack free after approximately 35 minutes.
10. Parts will be partially cured after 24 hours. Full cure and hardness does not take place until 5 to 6 days after application.
11. Finished goods may be shipped after 24 hours.
12. Clean tools and equipment with acetone or xylene.